Alloy 304 & 304L
- ALLOY 304 & 304L • UNS S30403 • WNR 1.4306
Alloys 304 (S30400) and 304L (S30403) stainless steels are variations of the 18 percent chromium – 8 percent nickel austenitic alloy, the most familiar and most frequently used alloy in the stainless steel family.
High strength, excellent corrosion resistance and minimized carbon content make Alloy 304 and 304L Stainless Steels useful for applications where welding is required. Uses include architectural mouldings and trim, welded components of chemical, textile, paper, pharmaceutical and chemical industry processing equipment.
Other advantages are its resistance to oxidation, excellent formability, ease of fabrication and cleaning, excellent strength to weight ratio and good toughness at cryogenic temperatures.
For severely corrosive environments,the lower content of Type 304L is preferred because of its greater immunity to intergranular corrosion.
- Available Tube Product form
- Straight
- Coiled
- Seamless
- Seam welded and cold redrawn
- Seam welded, cold redrawn and annealed
- Typical Applications
- Moisture seperator reheaters
- Feedwater tubes
- Stator bars
- Heat exchangers
- Industries predominantly using this Grade
- Nuclear and power
- General engineering
- Typical Manufacturing Specifications
- AMS 5566
- AMS 5569
- AMS 5647
- AMS-T-6845
- BS 10216 Pt 5
- ASTM A213
- ASTM A269
- ASTM A312
- ASTM A632
- MIL-T-8504
- MIL-T-8606
- Also individual customer specifications.
- Technical Data
Mechanical Properties
Temper | 304 | 304L | ||
Tensile Rm | 76 | ksi (min) | 70 | ksi (min) |
Tensile Rm | 517 | MPa (min) | 485 | MPa (min) |
R.p. 0.2% Yield | 31 | ksi (min) | 25 | ksi (min) |
R.p. 0.2% Yield | 207 | MPa (min) | 170 | MPa (min) |
Elongation (2” or 4D gl) | 40 | % (min) | 40 | % (min) |
Physical Properties (Room Temperature)
Specific Heat (0-100°C) | 500 | J.kg-1.°K-1 |
Thermal Conductivity | 16.2 | W.m -1.°K-1 |
Thermal Expansion | 17.2 | μm/μm/°C |
Modulus Elasticity | 193 | GPa |
Electrical Resistivity | 7.23 | Ohm-cm |
Density | 8.0 | g/cm3 |
Chemical Composition (% by weight)
Element | 304 Min | 304 Max | 304L Min | 304L Max |
C | - | 0.08 | - | 0.035 |
Mn | - | 2 | - | 2 |
Ni | 8 | 11.0 | 8 | 12.0 |
Cr | 18 | 20 | 18 | 20 |
S | - | 0.03 | - | 0.03 |
N | - | 0.1 | - | 0.1 |
Si | - | 0.75 | - | 0.75 |
P | - | 0.045 | - | 0.045 |